玻璃纤维增强材料43%,高拉伸强度, 良好的流动性, 良好的抗蠕变性, 抗溶剂性,齿轮, 草坪和园林设备,汽车的发动机罩下的零件, 动力/其它工具, 外壳

 

Vydyne® R543H NT

聚酰胺66

Ascend Performance Materials Operations LLC

Technical Data

 

产品说明

 

Vydyne R543H NT is general-purpose, 43% glass-fiber reinforced PA66 resin. Available in natural, it is an injection-molding grade resin that is lubricated for machine feed, flow and mold release.

 

Glass-reinforced Vydyne resins provide a higher heat distortion temperature, better resistance to creep, higher impact and better dimensional stability when compared with unreinforced PA66. These products have good chemical resistance to a broad range of chemicals, including many aliphatic and aromatic hydrocarbons found in most solvents, gasoline, hydraulic fluids, greases and machine oils.

 

Vydyne R543H NT resin has tensile strength and modulus properties just below aluminum and zinc and can replace these metals in numerous applications due to an excellent balance of properties. Reduction in production costs, energy consumption and part weight are key advantages of Vydyne glass-reinforced PA66 resins over aluminum and/ or zinc die-cast parts.

 

Vydyne R543H NT is formulated to minimize the oxidative and thermal degradation of the PA66 polymer when exposed to elevated temperatures for extended periods of time. Vydyne R543H NT provides improved retention of physical properties under exposure to long-term heat. The continuous operating use temperature is 275°F, with short-term peak temperatures as high as 475°F.

 

Typical Applications/End Uses: To come

 

总体

 

材料状态 • 已商用：当前有效

资料 1 •  Technical Datasheet

搜索 UL 黄卡 •  Ascend Performance Materials Operations LLC

•  Vydyne®

供货地区 • 北美洲 • 欧洲 • 亚太地区

填料/增强材料 • 玻璃纤维增强材料, 43% 填料按重量

添加剂 • 热稳定剂 • 润滑剂

• 尺寸稳定性良好 • 抗撞击性，良好 • 耐油性能

• 刚性，高 • 良好的抗蠕变性 • 耐油脂性能

特性 • 高拉伸强度 • 流动性高 • 热稳定性

• 高强度 • 耐化学性良好 • 润滑

• 抗溶剂性 • 耐汽油性 • 脱模性能良好

用途 • 草坪和园林设备 • 动力/其它工具 • 外壳

• 齿轮 • 汽车的发动机罩下的零件

机构评级 • ASTM D 4066 PA012G45 • ASTM D 6779 PA012G45

UL文件号 • E70062

外观 • 自然色

形式 • 粒子

加工方法 • 注射成型

物理性能 干燥 调节后的 单位制 测试方法

密度 1.50 -- g/cm³ ISO 1183

收缩率 ISO 294-4

垂直流动方向 : 23°C, 2.00 mm 0.90 -- %

流动方向 : 23°C, 2.00 mm 0.40 -- %

吸水率 ISO 62

23°C, 24 hr 0.60 -- %

平衡, 23°C, 50% RH 1.5 -- %

机械性能 干燥 调节后的 单位制 测试方法

拉伸模量 (23°C) 14800 11300 MPa ISO 527-2

拉伸应力 (断裂, 23°C) 225 170 MPa ISO 527-2

拉伸应变 (断裂, 23°C) 3.0 4.0 % ISO 527-2

弯曲模量 (23°C) 12500 9400 MPa ISO 178

弯曲应力 (23°C) 340 250 MPa ISO 178

泊松比 0.40 -- ISO 527-2

 

Vydyne® R543H NT

聚酰胺66

Ascend Performance Materials Operations LLC

冲击性能 干燥 调节后的 单位制 测试方法

简支梁缺口冲击强度 ISO 179

-30°C 13 14 kJ/m²

23°C 14 20 kJ/m²

简支梁无缺口冲击强度 ISO 179

-30°C 87 90 kJ/m²

23°C 92 95 kJ/m²

悬壁梁缺口冲击强度 ISO 180

-30°C 13 13 kJ/m²

23°C 13 19 kJ/m²

热性能 干燥 调节后的 单位制 测试方法

热变形温度

0.45 MPa, 未退火 260 -- °C ISO 75-2/B

1.8 MPa, 未退火 252 -- °C ISO 75-2/A

熔融温度 260 -- °C ISO 11357-3

线形热膨胀系数 ISO 11359-2

流动 : 23 到 55°C, 2.00 mm 1.6E-5 -- cm/cm/°C

横向 : 23 到 55°C, 2.00 mm 1.0E-4 -- cm/cm/°C

RTI Elec UL 746

0.750 mm 140 -- °C

1.50 mm 140 -- °C

3.00 mm 140 -- °C

RTI Imp UL 746

0.750 mm 130 -- °C

1.50 mm 130 -- °C

3.00 mm 130 -- °C

RTI UL 746

0.750 mm 140 -- °C

1.50 mm 140 -- °C

3.00 mm 140 -- °C

电气性能 干燥 调节后的 单位制 测试方法

体积电阻率 (0.750 mm) 1.0E+12 -- ohm•cm IEC 60093

介电强度 (1.00 mm) 20 -- kV/mm IEC 60243

耐电弧性 (3.00 mm) PLC 5 -- ASTM D495

漏电起痕指数 (3.00 mm) 400 到 599 -- V IEC 60112

高电弧燃烧指数(HAI) UL 746

0.750 mm PLC 0 --

1.50 mm PLC 0 --

3.00 mm PLC 0 --

高电压电弧起痕速率 (HVTR) PLC 1 -- UL 746

热丝引燃 (HWI) UL 746

0.750 mm PLC 4 --

1.50 mm PLC 3 --

3.00 mm PLC 4 --

可燃性 干燥 调节后的 单位制 测试方法

UL 阻燃等级 UL 94

0.750 mm HB --

1.50 mm HB --

3.00 mm HB --

灼热丝易燃指数 IEC 60695-2-12

0.750 mm 675 -- °C

1.50 mm 675 -- °C

3.00 mm 960 -- °C

 

Vydyne® R543H NT

聚酰胺66

Ascend Performance Materials Operations LLC

可燃性 干燥 调节后的 单位制 测试方法

热灯丝点火温度 IEC 60695-2-13

0.750 mm 700 -- °C

1.50 mm 700 -- °C

3.00 mm 750 -- °C

极限氧指数 25 -- % ISO 4589-2

补充信息 干燥 调节后的 单位制 测试方法

Automotive Materials - (thickness d = 1mm) + -- FMVSS 302

注射 干燥单位制

干燥温度 80.0°C

干燥时间 4.0hr

建议的最大回制料比例 25%

料筒后部温度 280 到 310°C

料筒中部温度 280 到 310°C

料筒前部温度 280 到 310°C

射嘴温度 280 到 310°C

加工（熔体）温度 285 到 305°C

模具温度 65.0 到 95.0°C

 

 

 

 

 

 